Titanium wire drawing is a metal plastic processing process in which wire rod or wire blank is pulled out from the die hole of wire drawing die under the action of drawing force to produce titanium wire with small section.
Titanium wire of different section shape and size can be produced by drawing. The surface is smooth, and the drawing equipment and mold are simple and easy to manufacture.When drawing superfine titanium wire with diameter less than 0.05mm, it is difficult to pass the die.
In order to improve the stability of the drawing process, reduce the number of breaking and passing the die, and improve the drawing production efficiency, the safety factor K value greater than 2.0 can be adopted.
Cold drawing is the most common drawing method used in titanium wire production. During hot drawing, the metal wire should be heated before entering the die hole.
The hot drawing method is mainly used for drawing high melting point metals such as tungsten, molybdenum and other metal wires.
According to the number of molds that the metal wire passes through at the same time in the drawing process, the drawing that only passes through one mold is a single pass, and the drawing that successively passes through several (2 ~ 25) molds is a multi-pass continuous drawing.
Single pass drawing line speed is low, productivity and labor productivity is low, often used for large diameter, low plasticity and special-shaped wire, wire drawing.
Please note that the specific details of the drawing process for titanium coiled wire can vary depending on the specific requirements, alloy composition, and equipment used. It is always recommended to consult with experienced professionals or manufacturers specializing in titanium wire production for precise process parameters and guidelines.